| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | ||
| 基本性能 | 密度 | --- | ISO 1183 | 1200 | Kg/m3 | |
| 吸水率 | 24hr in 23℃ | ASTM D-570 | 0.2 | % | ||
| 物理性能 | 透光率 | 3mm thick | ASTM D-1003 | 88 | % | |
| 折射率 | --- | ASTM D-542 | 1585 | --- | ||
| 阻燃性 | --- | UL 94 | V-2 | --- | ||
| 机械性能 | 悬臂梁冲击强度 | 带缺口 | ISO 179 | 12 | KJ/m2 | |
| 拉伸模量 | 1mm/min | ISO 527-1 and ISO 527-2 | 2400 | MPa | ||
| 拉伸屈服应力 | 50mm/min | ISO 527-1 and ISO 527-2 | 61 | MPa | ||
| 拉伸屈服伸长率 | 50mm/min | ISO 527-1 and ISO 527-2 | 6 | % | ||
| 拉伸断裂公称伸长率 | 50mm/min | ISO 527-1 and ISO 527-2 | >50 | % | ||
| 弯曲强度 | 2mm/min | ISO 178 | 92 | Mpa | ||
| 弯曲模量 | 2mm/min | ISO 178 | 2350 | Mpa | ||
| 悬臂梁冲击强度 | 没缺口 | ISO 179 | NB | KJ/m2 | ||
| 电气性能 | 表面电阻率 | --- | IEC600 | >1×1015 | Ω | |
| 体积电阻率 | --- | IEC 60093 | >1×1013 | Ω.cm | ||
| 介电常数 | 1MHz | IEC 60250 | 3 | --- | ||
| 介电常数 | 100Hz | IEC 60250 | 3.1 | --- | ||
| 介电损耗正切 | 100Hz | IEC 60250 | 10 | ×10-4 | ||
| 介电损耗正切 | 1MHz | IEC 60250 | 90 | ×10-4 | ||
| 耐电弧性 | --- | IEC 60112 | 225 | --- | ||
| 耐电压 | 短时间法 | IEC 60243-1 | 32 | MV/m | ||
| 加工性能 | 成型收缩率 | 平行方向 | --- | 0.5～0.7 | % | |
| 垂直方向 | 0.5～0.7 | % | ||||
| 热 性 能 | 热挠曲温度 | 1.80MPa | ISO 75-1 and ISO 75-2 | 128 | ℃ | |
| 热挠曲温度 | 0.45MPa | ISO 75-1 and ISO 75-2 | 141 | ℃ | ||
| 线膨胀系数 | 平行方向 | --- | ISO 11359-2 | 0.7 | ×10-4 | |
| 垂直方向 | ISO 11359-2 | 0.7 | ×10-4 | |||
| 维卡软化点 | 50℃/h 50N | ISO 308 | 148 | ℃ | ||
| 温度指数 | 电学式 | 厚度1.47mm | UL 746B | 125 | ℃ | |
| 冲击式 | 厚度1.47mm | UL 746B | 115 | ℃ | ||
| 非冲击式 | 厚度1.47mm | UL 746B | 125 | ℃ | ||